Compositions of inorganic-organic alloy with high nitrogen content polymers and their manufacture

ABSTRACT

Inorganic-organic alloy polymer adduct composition for waste water treatment, having the formula: 
     
         A·B·C·D 
    
     wherein 
     A is from 5% to 95% by weight of the total alloy composition, and is selected from the group comprising: polyhydroxyaluminumchloride, hydroxyaluminumchloride, polyhydroxyaluminumagnesiumchloride, polyhydroxyaluminumagnesium sulfate, polyhydroxyaluminumagnesiumsulfate, hydroxyaluminumsulfate, polyhydroxyaluminumzincoxidechloride, polyhydroxyaluminumchlorosulfate, polyhydroxymagnesiumchlorosulfate, polyaluminumferricchloride, polyaluminumferrouschloride, polyaluminumchloridesulfate, polyhydroxyaluminumchloridesilicate, and polyhydroxyaluminumsodiumsulfophosphate; 
     B is selected from the group comprising polymers or resins made from guanidine, dicyandiamide, or cyanoguanidine compounds; 
     C is an aqueous solution of cationic resin mixed with a reagent selected from polyalkylamines, polyethylenepolyamines, N-substituted ethyleneimines, polyquaternary compound, 1,3-bisquaternaryammonium compound, and polyquaternaryalkylamines; and 
     D is selected from the group comprising aqueous solutions of the quaternary ammonium compounds and their ethylenically unsaturated (co)polymerizable compounds incorporated therein.

BACKGROUND OF THE INVENTION

The present invention relates to compositions of matter, which may be used to purify industrial waste water and other industrial waste liquids, solids or semiliquids, chemicals, demulsification processes, in the paper industry (for sizing processes, drainage, retention, flotation), miniming industry, clay industry or other industries which have a waste water or waste liquid problem.

It is well known that guanidine resins or polymers are of lower molecular weight, and have very limited shelf life, in most cases less than 3 months, often only a few days or weeks. Low cationic charge polymers are of limited use in industrial water treatment of potable water. Treatment is very limited, since the free formaldehyde content is high. Most of the products can be used only as coagulants in connection with alum, AlCl₃, FeCl₃, Fe₂ (SO₄)₃ and mixtures of these, at a pH of from 6.0 to 9.0.

It has been found that reaction of guanidine, guanidine polymers or guanidine alkylamine/alkylamine polymers with inorganic adduct polymers and/or its guanidine derivative polymers alloy with organic alkyl or alkylene polyamine and adducts with inorganic adducts polymers will form very stable multi cationic or anionic polymers which can be used as coagulant and coagulant-flocculants with or without any electrolytes from a pH of 2 to a pH of 13.5.

These products can be used in any kind of industrial waste water, potable water, acid rain water purification, sludge coagulation and solidifications, or dust suppressant applications.

The inorganic-organic adduct polymers are twice as efficient as regular guanidine resins, having a shelf life from at least one year to four years, depending on the composition. The products produce low volume sludges, which relieve large volume disposal problems for the environment.

The invented compositions are made from inorganic polymers in reaction with guanidine polymers and their organic alloy with high nitrogen content compositions of polyamines, polyquaternized polymers, polyamides, and polyamine-polyamide polymers.

This invention generally relates to the novel of inorganic-organic alloy (co)polymers of the formula: ##STR1## where: Me_(m) ^(II) is a divalent cation group selected from Mg, Zn, Ca, Fe²⁺, and m=0 to 5;

Me_(n) ^(III) is a tri- or more valent metal, preferably Fe or Al, and n=1 to 20;

Aci is selected from the monovalent anionic group of (a) Cl, (b) Br, (c) I⁻, (d) NO₃ ⁻, (e) CH₃ COO⁻, and (f) a mixture of these (preferably Aci is Cl⁻);

PAM, PAD and PQAM stand for polyamine, polyamide and polyquaternized polymers;

p=0 to 75;

y=0 to 15;

x=preferably 0 to 95% by weight in compositions;

z=percentage by weight of the polyamine in the alloy composition, which can vary from 0 to 95%;

t=percentage by weight of the polyamide, which can vary from 0 to 95%;

t+z=percentage by weight of the mixture of polyamide-polyamine, which can vary in compositions from 0% to 95% by weight;

w=percentage by weight of the quaternary ammonium and/or allyltrialkylammonium compounds, which can vary from 0 to 95%; 2m+3n>2y+p; z>t

R₁ --refers to the bridge cationic and/or multiple organic cationic charges which can vary from 0% to 28% by weight;

R₂ --refers to the alkyl phosphonic acid esters, and or amine derivatives which will form phosphammonium cationic charge groups, which can vary from 0 to 28% by weight.

The invented compositions of matter are useful to purify industrial waste water (w.w.) and other industrial waste liquids, solids or semiliquids, from chemical plants, demulsification processes, paper industry (such as sizing processes, drainage, retention, flotation), mining industry, and clay industries.

DETAILED DESCRIPTION OF THE INVENTION

The present invention is an inorganic-organic alloy polymer adduct composition having the formula: A·B·C·D. Each component is described hereafter in detail.

COMPONENT A

The novel bloc(co)polymers alloy of inorganic polymers (A) is defined by any of the following general formulas, I(a) through I(f):

    [Me.sub.m.sup.II Me.sub.n.sup.III (OH).sub.p (SO.sub.4).sub.y (Aci).sub.(2m+3n)-p-2y ]                                  I(a)

wherein:

Me_(m) ^(II) is a divalent cation group selected from Mg, Zn, Ca, Fe²⁺ and m=0 to 5;

Me_(n) ^(III) is a tri- or more valent metal, preferably Fe or Al, and n-1 to 20;

Aci is selected from a monovalent anionic group consisting of (a) Cl⁻ (b) Br⁻, (c) I⁻, (d) NO₃ ⁻, (e) CH₃ COO⁻ or (f) a mixture of two or more of the foregoing, but preferably Aci is Cl⁻.

These products may be prepared by a variety of processes as described in U.S. patent application Ser. No. 646,012, filed Aug. 31, 1984, now U.S. Pat. No. 4,566,986.

    Al.sub.m (OH).sub.n X.sub.3m-n-2k (SO.sub.4).sub.k         I(b)

wherein:

X is sodium or potassium aluminate

k, m, n are positive numbers

    Al.sub.1-x Fe.sub.x.sup.III Fe.sub.y.sup.II (OH).sub.3+2y-2 (Hal).sub.z I(c)

wherein:

Hal=chlorine, bromine, iodine, or a mixture thereof;

(x+y)/(1-x)=about 0.2 to 1.5,

z<3+2y, and

(3+2y-2)/(3+2y)=about 0.24 to 0.67.

    Al.sub.m (OH).sub.x (SO.sub.4).sub.y (H.sub.2 PO.sub.4).sub.z I(d)

with the promise that the sum of x+2y +2 is 3; m and x are positive integers; and y and z are 0 and/or positive integers.

    M.sub.n e (OH).sub.m X.sub.3n-m                            I(e)

wherein:

m, n are positive integers

M_(n) e is a tri- or more valent metal

X is Cl⁻, CH₃ COO⁻, or NO₃.

I(f): Regular salts of aluminum, iron, titanium vanadium, chromium, antimonium, such as chloride, sulfates, phosphates, nitrates, acetates or mixtures thereof.

Inorganic adduct polymers, as the term is used in this specification, includes, without limitation:

1. Polyhydroxyaluminumchloride:

    Al.sub.4 (OH).sub.9 (Cl).sub.3, or Al.sub.8 (OH).sub.2 (Cl).sub.3, or Al.sub.11 (OH).sub.30 (Cl).sub.3 ;

2. Hydroxyaluminumchloride: Al₂ (OH)₅ Cl as ChlorhydrolTR-50, AstrigenTR-50;

3. Polyhydroxyaluminumagnesiumchloride: Al₃ Mg (OH)₉ (Cl)₂ ;

4. Polyhydroxyaluminumcalciumchloride: Al₇ Ca₀.04 (OH)₁₇.01 (Cl)₄ ;

5. Polyhydroxyaluminumagnesiumsulfate: Al₄ Mg(OH)₄ (SO₄)₃.5 ;

6. Hydroxyaluminum sulfate: Al₂ (OH)₄ (SO₄);

7. Polyhydroxyaluminumzincoxidechloride: Al₃ (OH)₃ ZnO(OH)(Cl)₅ ;

8. Polyhydroxyaluminum and/or magnesiumchlorosulfate:

    Al.sub.4 (OH).sub.6 (Cl).sub.4 (SO.sub.4);

    Al.sub.4 Mg (OH).sub.6 (Cl).sub.4 (SO.sub.4).sub.2 ; or

    Al.sub.3 Mg (OH).sub.6 (Cl).sub.3 (SO.sub.4);

9. Polyaluminumferic and/or ferrous chloride; ##STR2## 10. Polyaluminumchloridesulfate; and 11. Polyhydroxyaluminumchloro silicate.

COMPONENT B

Component B of the composition is guanidine, and/or dicyanodiamide and/or a cyanoguanidine compound, such as shown in Disclosure Document No. T965,001, is a resin guanidine, defined but not limited by any of the following formulas B(1) through B(7): ##STR3## where n is less than 100,000. ##STR4## where R₁ refers to the bridge cationic charge and/or multiple organic cationic charges, which may vary from 0% to 28% pbw. of the composition;

R₂ refers to the alkyl phosphonic acid ester and/or amine derivatives of phosphonic acid, which will form the phosphonium cationic charge groups, from 0 to 28% bw of the composition. ##STR5## wherein: in B(2): R₁ refers to the bridge cationic charge and/or multiple organic cationic charges of mixture of thereof, such as but not limited to: ##STR6## In B(3): R² refers to the dialkyl hydrogen phosphite, ester amines, phosphorus acid and its esters or salts, H₃ PO₄ and its salts, such as sodium dihydrogen phosphates, including the following:

(a) dimethyl hydrogen phosphite;

(b) hydroxyethylidene-1,1-diphosphonic acid and its salts (of Li, Na, K, and NH₄)

(c) diethylenetriaminepentmethylene phosphonic acid and its salts (Li, Na, K, NH₄)

(d) carbonyl diamidetetramethylene phosphonic acid and its salts (Li, Na, K, NH₄)

(e) N(2-aminoethyl piperazine) phosphonic acid and its salts (Li, Na, K, NH₄)

(f) N(2-aminoethylmorpholine) phosphonic acid and its salts (Li, Na, K, NH₄)

(g) 2 (heptyl-2-imidazoline) phosphonic acid and its salts (Li, Na, K, NH₄)

(h) phosphoric acid and its salts, such as sodiumdihydrogenphosphate,

(i) methylene phosphonic acid substituted amide>N--CH₂ PO₃ H₂ made from Urea (U)-Formaldehyde (F)-phosphorus acid and/or mixture of phosphorus acid/hydrochloric acid where the HCl is used as a catalyst from 0.25 to 0.5 mole, the mole ratio of U--CH₂ O--H₃ PO₃ being 1:3.50:3.25.

The products symbolically represented as:

    [(A)]+[B(2) and/or B(3)]

can give strong (co)polymers charged with long pot life and high potential polyelectrolytes. The product will have on the macromolecular chain graft the phosphonium anion and/or it will have on the chain (or between two or more macromolecular chains attached the polyfunctional ammonium cationic charge unit(s) having as permanent unit the chlorine (Cl⁻) and/or sulfate (1/2SO₄)²⁻ permanent graft. In the present invention, chemically quaternized products are attached to form a cationic guanidine through bridges of component B as shown in the formulas B(2) and B(3).

For instance, one of the examples could be suggested by using in the reaction the products;

    B(1)+B(2)(a)+B(3)(a) or B(1)+B(2)(b)+B(3)(a)

and a polyammonium salt charged will be formed such as: ##STR7## In C and D, the inorganic-organic alloy could be further reacted and/or mixed quaternary polyamines, with or without alkylene polyamines and polyamides and/or mixture of the polyamines (PAM) with polyamides (PAD), (PQAM) to generate the 3rd and 4th segment of the generic formula (I).

COMPONENTS C AND D

The polyamine defined by C and D incorporate the water soluble polymer condensation products of alkylamines, polyalkyl amines, ammonia, or a mixture of them, with polyfunctional aliphatic dihalides or halohydrins which may, if desired, be further reacted with urea or with urea-formaldehyde condensation products and/or melamineformaldehyde colloidal condensation products and/or dimethylol urea, the final product being water soluble.

Examples of polyfunctional aliphatic compounds are ethylenedichloride, alphadichlorhydrin, dibromohydrin, diiodohydrin, epichlorohydrin, epibromhydrin, epiiodohydrin, diepi-iodohydrin. The alkylene polyamine used in preparing the cationic reaction products employed in practicing my invention are well-known compounds corresponding to the formula H₂ N(C_(n) H_(2n) HN)_(x) H in which x is one or more typical amines of this class of alkylene polyamines, such as diethylenetriamine, triethylenetriamines, tetraethylenepentamine and the corresponding polypropylenepolyamines and polybutylenepolyamines. This class also includes polyalkylenediamine such as N,N,N',N'-tetramethylethelynediamine (TMEDA); tetramethylenebutanediamine (TMBDA) N,N,N',N',2 pentamethyl-1,2-propanediamine; 1,1,3,3-tetramethylguanidine; N,N,N',N'-tetramethyl-1,6-hexane diamine; N,N,N',N'-tetramethyl-1,3-propane diamine; and 1,1,3,3-tetramethylurea.

Such products are described in the following U.S. Patents and the references cited in them:

    ______________________________________                                         U.S. Pat.    Re 28 807      3,855,299                                          2,765,229    3,894,945                                                         2,969,302    3,920,546                                                         3,372,129    3,958,931                                                         3,468,818    4,052,259                                                         3,738,945    4,059,515                                                         3,751,474                                                                      ______________________________________                                    

In component D, other quaternary ammonium compounds and an ethylenically unsaturated copolymerizable compound are incorporated as the segment (PQAM) of the generic formulae: ##STR8## or other structures as are described in U.S. Pat. Nos. 3,311,594, 3,645,954, 3,585,148, 2,926,161, 2,923,701, 4,053,512, 3,032,539, and 2,550,652.

The inorganic adduct polymers which are multianions can display the monoactivity charges of (Cl⁻) or 1/2 SO₄ ²⁻ by the multivalent metal anion system generating more active flocculants and/or coagulants.

For instance, if an inorganic adduct polymer such as aluminumhydroxysulfate is reacted with polydiallydimethylammoniumchloride, the chlorine anion (Cl⁻) will be displayed by the multi anion, thus: ##STR9## where the dissociation constant (k_(d)) is greater than association constant (k_(a)); ##STR10## where R₁ and R₂ represent hydrogen, methyl and ethyl radicals, R₃ and R₄ each represents alkyl, alkoxyalkyl, hydroxyalkyl radicals having one to 8 carbon atoms and Y represents an anion and 2 complex anions, such as methosulfate, ethosulfate, chlorine, bromine and iodine.

The polyamide and/or polyamine are made by reaction of dibasic carboxylic acid, such as adipic acid, with epsilon caprolactam and/or diethylene triamine and/or polyalyleneamines having C₄ -C₈, and/or by reaction of dibasic carboxylic acid first reacted with polyalkylenepolyamide containing the recurring groups:

    --NH (C.sub.n H.sub.2n HN).sub.x CORCO--

where n and x are each 2 or more, and R is a divalent hydrocarbon radical of dibasic carboxylic acid. The long chain polyamide is then reacted with epichlorohydrin (EPI) and/or other haloderivative products mentioned above. The Group of Components D can include products with or without N-substituted polyacrylamide quaternary ammonium salts (co)polymers, or polyallyltrialkylammonium (co)polymers, such as polydiallyldimithylammoniumchloride (POLYDADMAC). (co)polymers of hydrochloride of N,N diallylglycine, polydiallylamine are also incorporated into the present invention.

DETAILED DESCRIPTION OF THE INVENTION

It is known that guanidine resins can be made either alkaline or acidic in pH. In either case, the products are not of high molecular weight and have a very short pot life. The jelletion effect is very common to all of them. The guanidine resins are very sensitive to water, therefore water must be added slowly. It is known that even in presence of Lewis acid catalyst, such as ammonium chloride, ammonium sulfate, and/or ammonium nitrate, very few anions such as chlorine, sulfate and/or nitrate are attracted by the molecule to form stable ammonium type products.

The guanidine polymes and/or resins are made in the pH range from 0.5 to 7.0, but preferably about pH 5.5. These polymers can be made by reacting the guanidine and/or dicyandiamide with urea, ethylene diamine, and/or triethylenetetramine hydrochloride, ammonium chloride, ammonium sulfate, ammonium nitrate, formaldehyde and/or paraformaldehyde, hydrochloric acid. The stable guanidine polymers can be made by co-reacting the guanidine monomers and/or dicyandiamide in the presence of mono and/or polyfunctional amines or other HCl salts such as:

(B):

(1) Aminoethylethanolamine

(2) Monoethanolamine

(3) Diethanolamine

(4) Hydroxyethylethylenediamine

(5) Hydroxypropylethylenediamine

(6) Guanidine-bis-N,N'-hydroxyethylethylenediamine

(7) N,N'-hydroxyethylaminoethylurea

(8) N,N'-bishydroxyethylhydroxymethylaminoethylurea

(9) N,N'-bisguanidineethlenediamine

(10) N,N'-bishydroxymethylethylethylenediamine

(11) N,N'-bisguanilurea

(12) 2,(2-aminoethoxy)ethanol

(13) Polyethyleneamine with Mw≧500,000, preferably 100,000

(14) Polydiallyldimethylammoniumchloride (MW≧500,000)

(15) Polyalkylamine, with Mw less than 500,000, preferably less than 100,000

(16) Water soluble melamine sulfonate products such as those made from melamine-formaldehyde sodiumbisulfite are preferably incorporated in the present invention, having been described in U.S. Pat. No. 2,407,599

(17) Polyacrylamide-amino plast resin compositions as described in U.S. Pat. No. 2,862,901

(18) Polyalkylamine ammonium salts and/or aminoalkylurea represented generically by the formula: ##STR11## where n is an integer from 2 to 4, m is an integer from 1 to 4, and R is H, an alkyl, or an hydroxyalkyl group of 1-2 carbon atoms. The aminoalkyl groups set forth in the formula include:

CH₂ CH₂ NH₂ ; CH₂ CH₂ --NH--CH₂ CH₂ --NH₂ ; CH₂ CH₂ --NH--CH₂ CH₂ NH--CH₂ CH₂ OH; and CH₂ CH₂ --NH--CH₂ CH₂ NH--CH₂ CH₂ NH--CH₂ CH₂ NH₂ ;

which are disclosed in U.S. Pat. No. 2,616,874.

(19) Sulfamic acid/ethylene urea reaction products having generically the formula of: ##STR12## where n≦250 are incorporated in the present invention. (20) Benzoguanamine (1 mole) with formaldehyde (1.2-3.5 moles) are incorporated in the present invention.

(21) Polydiallyldimethylammoniumchloride (PDADMAC) and its copolymers having a Mw≦500,000 are incorporated in the present invention.

(22) B-hydroxyethylsulfone and condensation products of sulfonated dihydroxydiphenylsulfones or sulfonated dihydroxydiphenols lower alkylaldehydes or lower aliphatic aldehydes are incorporated in the present invention.

(23) With and/or without alkylamines or polyalkyl or cycloalkylamines or bis tertiaryalkylurea amines, having C₂ -C₈ atoms bridges between nitrogen atoms such as ethylenediamine, diethylenetriamine or others defined by the formula:

    H.sub.2 N (C.sub.n H.sub.2n HN).sub.x H

where x is one or more or with tri or tera substituted hexamethylene triamine or piperazine in the presence of the polyfunctional an reactive ammonium quaternized products, in particularly with Cl⁻ or 1/2SO₄ ²⁻, such as:

(23) 1. ##STR13## or (C₆ H₁₅ NOCl) (23) 2. ##STR14## or (C₆ H₁₄ NOCl) by reacting trimethylamine (1 mole) with Epichlorhydrin (EPI)(≧3.5 moles) and/or bis tertiaryalkylenealkylamine with (EPI).

(23) 3. ##STR15## or (C₁₃ H₃₀ N₂ O₃ Cl₄) (23) 4. ##STR16## (made from dimethylaminehydrochloride, dimethylamine and epichlorhidrin (EPI).

(23) 5. ##STR17## or (C₁₂ H₂₆ N₂ O₂ Cl₂) (made from NN,N,N'-tetramethylethylene diamine and epichlorohydrin (EPI)

(23) 6. ##STR18## or (C₁₆ H₃₆ N₂ O₆ Cl₂ S) or (C₁₆ H₃₆ N₂ O₂ Cl₄) (made by reaction of N,N,N',N' Tetramethylhexamethylenediamine in reaction with epichlorohydrin and sulfuric acid/or hydrochloric acid).

The inorganic adducts polymers described by formulae (A) or (I/a to I/e) and the regular salts as described by I/(8) can be reacted with guanidine (co)polymers made from wide molar ratios between guanidine and/or dicyandiamideformaldehyde-ammonium chloride such as:

0.356-2.0; 0.490-5.0; 0.5-2.0

and/or in presence of alkylamine in the range:

0.5-4.0; 1.5-9.0; 0.3-2.0; 0.05-0.5

The most preferable reactant mole ratios of guanidine and/or dicyandiamide to formaldehyde to ammonium chloride are:

1.0-2; 2-4; 1-2

The inorganic adduct polymers as described above, and/or regular salts of trivalent or higher metals can be reacted with guanidine (co)polymers with polyamine-polyamide organic alloys to form stable high potential coagulants-flocculants polymers. For high stability, the polyamide (PAD) and polyamine (PAM) are recommended to be in the weight ratio of:

    ______________________________________                                         Polyamide (PAD)                                                                               Polyamine (PAM)                                                                              Stability                                         ______________________________________                                         5.00 pbw       1.00 pbw      yes                                               4.950 pbw      1.00 pbw      yes                                               4.900 pbw      1.00 pbw      yes                                               4.830 pbw      1.00 pbw      yes                                               3.970 pbw      1.00 pbw      yes                                               ______________________________________                                    

The inorganic polymers and/or regular salts as described above can be used from 5% to 95% by weight and the polymine and/or polymide and/or polyamide/polyamine alloys can be used from 5% by weight to 95% by weight, to obtain stable complex adducts.

In the case of the reaction between inorganic adducts polymers and the guanidine polymers and its alloys of polyamine and/or polyamide/polyamine the weight percentage can be from:

5-95% by weight of inorganic polymers

0-95% by weight guanidine polymers, and/or

5-95% by weight of inorganic polymers

70-0% by weight of guanidine polymers

0-95% by weight of polyamine and/or polyamide/polyamine, and/or polyamide.

In the case of inorganic polymers and polyamine and/or polyamide/polyamine, and/or polyamide, the percentage by weight can be from:

0% to 95% of polyamine and/or polyamide/polyamine, and/or polyamide.

95% to 5% of inorganic polymers, quaternary ammonium and/or allyltrialkylammonium compounds.

The multi charges complex adduct polymers flocculant should be used in an effective amount which is readily determinable in use. This statement is well explained in the case of the multiple cationic charge of polyamine polymers described in U.S. Pat. No. 3,894,945.

The coagulation performance is determined by the turbidity test described in ASTM D2035-68.

The invented products and processes for their formation along with relevant data are presented below. It will be understood that these examples are not intended as limiting the invention, but as examples of the operation of the invention.

EXAMPLE NO. 1

A 2,000 ml resin kettle flask was equipped with condenser, a mechanical stirrer, a thermometer and an additional funnel. To the flask the following was added in order:

    ______________________________________                                         1.    37% Formaldehyde                                                                               541.5  g      6.668 moles                                2.    Dionized water  50.0   g      2.777 moles                                3.    Dicyandiamide   280.0  g      3.333 moles                                4.    Ammonium chloride                                                                              178.5  g      3.334 moles                                5.    Mixing was started.                                                      6.    The reaction is endothermic followed by a strong                               exothermic reaction.                                                     7.    Let the exotherm go no higher than 90° C., preferably                   80 to 85° C.                                                      8.    When the exothermic reaction is over, hold the reaction                        at 80-85° C. for an additional 3 hours.                           9.    Cool to 25-30° C.                                                 10.   Adjust the product Sp. Gravity to 1.150 to 1.200 g/ml,                         having pH = 3.0 to 4.0.                                                  11.   46.6g HCl (18%) was added to the 500 g of the above                            product.                                                                 12.   Agitation is continued for additional 15 minutes.                        13.   To the highly protonized polymer, 120 g of 25%                                 aluminum sulfate was added during a 15 minute period.                    14.   The agitation was continued for an additional                                  30 minutes.                                                              15.   At the end of this time the resultant product was                              drained off, having:                                                     pH = 1.9                                                                       Specific Gravity = 1.180 g/cc                                                  Appearance =  light yellow, transparent solution.                              ______________________________________                                    

EXAMPLE NO. 2

Steps 11 through 15 of Example No. 1 were repeated substituting 46.6g of dionized water for the HCl, and using 120 g of 10% aluminum sulfate (alum). The process produced a light yellow solution having:

pH=3.54

Sp. Gravity=1.144 g/cc

Appearance=water color, tint yellow blue.

EXAMPLE NOS. 3 through 15

Steps 11 through 15 of Example No. 1 were repeated by reacting 75% by weight of the polymer with 18% by weight of the following inorganic polymers under the conditions set forth in Table No. 1.

                                      TABLE NO. 1                                  __________________________________________________________________________          Polymer                                                                               Inorganic adduct        Time in                                    Ex. No.                                                                             75% bw polymer used     Temperature                                                                           minutes                                    __________________________________________________________________________     3    Ex. No. 1                                                                             Al.sub.4 (OH).sub.9 (Cl).sub.3                                                                  25-30° C.                                                                      30                                              (Steps 1-10)                                                              4           Al.sub.2 (OH).sub.5 Cl                                                                          25-30° C.                                                                      30                                         5           Al.sub.2 (OH).sub.4 SO.sub.4                                                                    25° C.                                                                         30                                         6           Al.sub.3 Mg(OH).sub.9 (Cl).sub.2                                                                25-30° C.                                                                      30                                         7           Al.sub.7 Ca.sub.0.04 (OH).sub.17,01 (Cl).sub.4                                                  30° C.                                                                         40                                         8           Al.sub.4 Mg(OH).sub.5 (SO.sub.4).sub.3.5                                                        25-30° C.                                                                      30                                         9           Al.sub.3 (OH).sub.3 ZnO(OH)                                                                     25-30° C.                                                                      30                                         10          Al.sub.4 (OH).sub.6 (SO.sub.4).sub.3                                                            25-30°C.                                                                       30                                         11          Al.sub.4 Mg(OH).sub.6 (Cl).sub.4 (SO.sub.4).sub.2                                               25-30° C.                                                                      40                                         12          Polyaluminumchlorosulfate                                                                       25-30° C.                                                                      30                                                     (PACS)                                                             13          AlFe.sub.0.25 .sup.II Fe.sub.0.25 .sup.III (OH).sub.2.12                       (Cl).sub.2.13    25° C.                                                                         40                                         14          Al.sub.2 Fe.sub.2 (OH).sub.3.32 (Cl).sub.6.68                                                   25° C.                                                                         40                                         15          Polyhydroxyaluminumchloro-                                                     silicate         25° C.                                                                         20                                         __________________________________________________________________________

EXAMPLE NO. 16

To the reactor described in Example No. 1, the following were charged:

    ______________________________________                                         1.     Dicyandiamide 240    g      2.857                                                                               moles                                  2.     37% Formaldehyde                                                                             490    g      6.034                                                                               moles                                  3.     Dionized water                                                                               90     g      5.0  moles                                  4.     Ammonium chloride                                                                            140    g      2.616                                                                               moles                                  ______________________________________                                    

Steps 5 through 7 of Example No. 1 were repeated, then:

8. After 2 hours reaction time, the temperature was raised to 90°-95° C., preferably to 90° C.

9. 20g/or 0.106 mole of 3-chloro-2-hydroxypropyl trimethyl ammoniumchloride (C₆ H₁₅ NOCl) (HPTMAC) (B/IIa) was charged to the reactor during 3 minutes.

10. The reaction was continued at 90° C. for 60 minutes.

11. The product was cooled to 25°-30° C., when water colored polymer was obtained with:

pH=3.55

Sp. Gravity=1.195

Solids=52%

Viscosity=105 centipoises

12. To 500g of the above product was added 7.977g of HCl (18%), then during a 10 minute period, 64.22g of 25% hydroxyaluminumchloride.

13. The agitation is continued for 30 minutes, when 25 g of dionized water was slowly added to the reactor.

14. The product was mixed for 5 minutes.

15. At the end of this time the product was drained off, having:

pH=2.8

Sp. Gravity=1.160 g/cc

Solids=52%

Appearance=light yellow color with blue collodal tint.

EXAMPLE NO. 17

Steps 12 through 15 of Example No. 1 were repeated by substituting hydroxyaluminumchloride with the inorganic adducts polymer/or and inorganic salts as set forth in Table No. II.

                  TABLE NO. II                                                     ______________________________________                                                                         Temp. Time re-                                 Ex.  Polymer   Inorganic adduct in    action in                                NO.  75% bw    Polymers used - 18% bw                                                                          °C.                                                                           minutes                                  ______________________________________                                              Ex. No. 15                                                                     Steps 1-11                                                                17             Al.sub.8 (OH).sub.2 (Cl).sub.3                                                                  25-30 30                                       18             Al.sub.3 Mg(OH).sub.9 (Cl).sub.2                                                                30    30                                       19             Al.sub.4 Mg(OH).sub.5 (SO.sub.4).sub.3.5                                                        25-30 30                                       20             NaH.sub.2 PO.sub.4 or H.sub.3 PO.sub.4                                         sodium-                                                                        tripolyphosphate solution                                                                       25-30 30                                       21             20% aq MgCl.sub.2 or 20%                                                                        25    30                                                      aq CaCl.sub.2                                                   22             30% AlCl.sub.3   25-30 30                                       23             Polyhydroxysodium-                                                             aluminum                                                                       sulfophosphate   25-30 45                                                      (Al.sub.2 O.sub.3 = 10%)                                        ______________________________________                                    

EXAMPLE NO. 16

The conditions of Example No. 15 were repeated by substituting for the cationic monomer (C₆ H₁₅ NOCl), 33.85g 0.106 mole of the polyfunctional cationic monomer described by the formula mentioned above (C₁₃ H₃₀ N₂ O₂ Cl₂) (B II/c). At the end of the step No. 12, water colorless product is obtained, having.

pH=4.0

Sp. Gravity=1.210 g/cc

Solids=55%

Viscosity=85 cps.

To 910g of the above product, 109g of polyhydroxyaluminumchloride (Al₄ (OH)₉ (Cl)₃) was added over a period of 10 minutes and then reacted for 30 minutes. A product having a light yellow color with blue colloidal tint was produced, having:

pH=2.5

Sp. Gravity=1.190 g/cc

Solids=49%

EXAMPLE NO. 24

The conditions of Example 15 (Steps 1 to 11) were repeated. Then the following steps were taken:

12. The product was cooled to 30°-35° C. when 20g of dimethylhydrogenphosphite (DMP) (B III/a) was added over a 10 minute period.

13. The agitation was continued for an additional 30 minutes.

14. The mixture was cooled to 25°-30° C. when a colorless liquid was obtained.

The polymer with double anion charge, ammoniumchloride and phosphonium, is obtained, having: pH=3.5; Sp. Gravity=1.193 g/cc; Solids=53%.

750g of the above product was diluted with 150g of dionized water. To this mixture was added 100g of 10% aluminum sulfate, over a 15 minute period, the reaction being continued for an additional 30 minutes. The resulting product has:

pH=2.9

Sp. Gravity=1.180 f/cc

Solids=50%

EXAMPLE NO. 25

To the reactor described in Example No. 1 was charged:

    ______________________________________                                         (1)    Dicyandamide     198    g     2.238                                                                               moles                                (2)    Monoethanolamine 20     g     0.237                                                                               moles                                (3)    37% Formaldehyde 320    g     4.064                                                                               moles                                (4)    Dionized water   72     g     4.0                                       (5)    Ammonium Chloride                                                                               114    g     2.131                                     ______________________________________                                    

Step Nos. 5 to 9 of Example No. 1 were followed, then:

(8) The product has:

pH=4.1, Sp. Gr.=1.228 g/cc, Solids=62%

(9) The above product was diluted to 45% solids with a specific gravity of 1.154 g/cc.

(10) To 438.45 g of the polymer made is added under agitation 3.05 g of HCl(18%) and mixed for 10 minutes.

(11) Then 58.45 g of 25% alum was added during a 10 minute period and reacted for an additional 30 minute period at 25°-30° C. It resulted in a product having:

pH=3.05,

Sp. Gr.=1.140 g/cc,

Solids=48%,

Appearance=light yellow tint blue color

EXAMPLE NO. 26

The conditions of Example No. 25 (steps 1 to 9) are repeated by substituting alum with 25% aluminumhydroxy chloride. The product has:

pH=2.8,

Sp. Gr.=1.160 g/cc,

Solids=47%,

Appearance=clear liquid with light blue tint colloidal color.

EXAMPLE NO. 27

The conditions of Example No. 26 are repeated by substituting the hydroxyaluminum chloride with 25% solution of polyhydroxyaluminummagnesiumchloride (PHAMC) Al₃ Mg(OH)₉ (Cl)₂, made from powder. The end product has:

pH=2.5,

Sp. Gr.=1.140 g/cc,

Solids=45%,

Appearance=clear liquid which after 3 hours turns into a stable light blue colloidal color.

EXAMPLE NO. 28

The conditions of Example No. 27 are repeated by substituting the (PHAMC) with polyhydroxyaluminumzincoxide chloride Al₃ (OH)₃ ZnO(OH)(Cl)₅ or (PHAZOCl). The product has:

pH=1.8,

Sp. Gr.=1.185 g/cc,

Solids=43%

Appearance=light yellow with a blue tint color.

EXAMPLE NOS. 29-44

The conditions for Example Nos. 29-44 are repeated by substituting the monoethanolamine with one of the following products or (1:1) mixture of them.

    __________________________________________________________________________          Product - Nitrogen Co Catalyst                                                                          Reaction                                         Ex. No.                                                                             Derivative         HCl (50/50)                                                                          Conditions                                       __________________________________________________________________________     29   Ethylene diamine   Yes   4 hrs.                                                                             90-95° C.                             30   Ethylene diamine HCl     1hrs.                                                                              80-85° C.                                                           3 hrs.                                                                             90-95° C.                             31   Diethanol amine    Yes   4 hrs.                                                                             90-95° C.                             32   Aminoethylethanolamine                                                                            Yes   4 hrs.                                                                             90-95° C.                             33   Hydroxyethylethylenediamine                                                                       Yes   4 hrs.                                                                             90-95° C.                             34   Hydroxypropylethylenediamine                                                                      Yes   4 hrs.                                                                             90-95° C.                             35   Guanidine-bis-N,N'--hydroxy-                                                                      Yes   1 hrs.                                                                             80-85° C.                                  ethylenediamine          3 hrs.                                                                             90-95° C.                             36   N,N'--Bisguanidineethylene-                                                                             1 hrs.                                                                             80-85° C.                                  dimaine            Yes   3 hrs.                                                                             90-95° C.                             37   N,N'--Hydroxymethylethylene-                                                                      Yes   1 hrs.                                                                             80-85° C.                                  diamine                  3 hrs.                                                                             90-95° C.                             38   N,N'--bisguanilurea                                                                               Yes   4 hrs.                                                                             90-95° C.                             39   2(2-aminoethoxy)ethanol                                                                           Yes   3 hrs.                                                                             80-85° C.                                                           1 hrs.                                                                             90-95° C.                             40   Polyethyleneimine  Yes   2 hrs.                                                                             80-85° C.                                  (Mw 100,00)              2 hrs.                                                                             90-95° C.                             41   Polydially Dimethylammoniumchloride                                            (Mw = 500,000)     Yes   0.5 hrs.                                                                           30-40° C.                             42   N,N'--Dishydroxymethyl                                                                            Yes   1 hrs.                                                                             80-85° C.                                  ethylenediamine          2 hrs.                                                                             90-95° C.                             43   2-amino-2ethyl-1-1,3 pro-                                                                               1 hrs.                                                                             80-85° C.                                  panediol                 2 hrs.                                                                             90-95° C.                             44   Tris (hydroxymethyl)-    1 hrs.                                                                             80-85° C.                                  aminomethane             2 hrs.                                                                             90-95° C.                             __________________________________________________________________________

To the reactor described in Example No. 1 is charged:

    ______________________________________                                         1.  Dicyandiamide      250    gr.  2.976                                                                               moles                                  2.  37% Formaldehyde   480    gr.  5.911                                                                               moles                                  3.  Dionized water     45     gr.  2.90 moles                                  4.  N,N'--bisguanidineethylene-                                                    diamine            20     gr.  0.091                                                                               moles                                  5.  HCl (18%)          25     gr.  0.205                                                                               moles                                  6.  Ammonium chloride  160    gr.  2.991                                                                               moles                                  ______________________________________                                    

Step numbers 6 and 7 of Example No. 1 are followed, with the exception that the mixture is reacted for 1 hour at 80°-85° C., followed by 3 hours at 90°-95° C. The resulting product has the following characteristics:

pH=3.2; Sp. Gr.=1.214 g/cc; Solids=60%

8.-803.10 g. of this product is treated with 26.6 g of HCl (30%) and reacted for 10 minutes. The 170.3 g of polyhydroxyaluminum calciumchloride (Al₇ Ca₀.04 (OH)₁₇.01 (Cl)₄) having a pH=2.45 and Sp. Gr.=1.402 g/cc, is added during 10 minutes at 25°-35° C. The composition is reacted for 30 minutes and then cooled to room temperature. The resulting product has:

pH=3.38

Sp. Gr.=1.206 g/cc

Appearance=transparent, with light yellow tint.

EXAMPLE NO. 45

The conditions of Example No. 30 were repeated by substituting in Step Number 7 the polyhydroxyaluminumcalciumchloride with polyhydroxyaluminummagnesiumsulfate (PHAMS) Al₄ Mg(OH)₅ (SO₄)₃.5, having:

pH=2.55,

Sp. Gr.=1.320 g/cc,

Solids=38%

To 801.50 gr. of polyamine made as in steps 1 to 6 of Example No. 30, is added 198.5 gr. of (PHAMS) during 15 minutes at 25°-30° C. The reaction is continued for an additional 30 minutes. The end product has the following properties:

pH=2.95

Sp. Gr.=1.211 g/cc

Appearance=water color with a clean light yellow tint reflection.

EXAMPLE NO. 46

To the reactor described in Example No. 1 was charged at room temperature:

    ______________________________________                                         1.  Dicyandiamide     168     g     2    mole                                  2.  Hydrochloride acid (37%)                                                                         486.11  g     4.925                                                                               mole                                  3.  Dionized water    13.89   g     0.772                                                                               mole                                  4.  Start mixing                                                               5.  The reaction is exothermic.                                                6.  Let the exotherm go no higher than 80-85° C.                            and hold for 1 hour.                                                       7.  To the reactor was added 486 g (5.985 mole) of 37%                             formaldehyde and the reaction was heated to 90-95° C.                   then was held for 5 hours.                                                 8.  Cool to 25° C. when a polyguanidineammoniumchloride                     was made (PGAC)                                                            9.  At the end of this time the product was drawn off                              having:                                                                    pH = 0.85, Sp. Gr. = 1.240 g/cc., Solids = 53% ,                               Appearance = water color product.                                              ______________________________________                                    

To 300 g of this product was added during 5 minutes 30 g. of polyamine (made from epichlorhydrin-dimethylamine-ethylendiamine, as described in Example No. 3 of U.S. Pat. Re 28,807.)

Under agitation to the above mixture was added during 10 minutes 30 g of hydroxyaluminumchloride (40% aq. solution). The reaction was continued for 30 minutes when stable viscosity and pH was obtained. The product has:

pH=1.3

Sp. Gr.=1.174 g/cc

Solids=45%

Appearance=light yellow to amber color

EXAMPLE NO. 47

To 300 g of the polyhydroxyaluminumagnesium sulfate [Al₄ Mg(OH)₅ (SO₄)₃.5 ] was added 30 g. of aluminumhydroxychloride (40% aq.) during 10 minutes and mixed until the pH became constant, forming polyhydroxyaluminumagnesiumchlorosulfate as inorganic polymer. To this composition under agitation was added 30 g of polyguanidineammoniumchloride of Example No. 46 and mixed for 45 minutes. The end product has:

pH=2.65,

Sp. Gr.=1.279 g/cc,

Solids=40%,

Appearance=light yellow to amber color.

EXAMPLE NO. 48

To the reactor described in Example No. 1 was charged:

    ______________________________________                                         1.    Dicyandiamide  164     g     1.952                                                                               moles                                  2.    Urea           60      g     1.0  moles                                  3.    37%            243.60  g     2.993                                                                               moles                                  4.    Ammonium chloride                                                                             25.2    g     0.467                                                                               moles                                  5.    Start agitation                                                          6.    The endotherm of the reaction dropped to 9° C., followed by       7.    The exotherm reaction was kept below 65° C.-70° C.         8.    To this composition was added 222.57 g (1.831 moles)                           of HCl (30%)                                                             9.    The composition was slowly heated to 90-95° C., then was                reacted for 4 hours.                                                     10.   The product was cooled down when water colored product of                      polyguanylureidoammoniumchloride was obtained                                  (PGUAC)                                                                  11.   The product at this point has:                                                 pH = 3.70, Sp.Gr. = 1.222 g/cc, Solids = 53%, Appearance = water               color.                                                                   12.   To 425 g. (PGUAC) of the above product under agitation was                     added 11 g of HCl (18%).                                                 13.   The agitation was continued for 15 minutes until the                           pH remained constant.                                                    14.   During a 10 minute period was added 65 g of 20%                                aluminumhydroxychloride                                                  15.   The reaction was continued for 20 minutes when the                             inorganic-organic alloy polymer was produced with:                       pH = 2.6,                                                                      Specific Gravity = 1.238 g/cc                                                  Solids = 45%,                                                                  Appearance = water color with colloidal blue refraction.                       ______________________________________                                    

EXAMPLE NO. 49

To the 300 g of the product made in Example No. 46 was added 100 g of dionized water. Agitation continued. During a 5 minute period was added 42 g polyethyleneimine (PEI) with very high molecular weight. Then under high agitation during 10 minute period was added 100 g of hydroxyaluminumchloride (Al₂ (OH)₅ Cl(HAlCl)). After 30 minutes the pH remained constant and the organic-inorganic alloy polymers were obtained, having:

pH=2.70,

Specific Gravity=1.149 g/cc,

Solids=35%

Appearance=yellow color.

EXAMPLE NO. 50

The conditions of Example No. 40 were repeated by substituting for aluminumhydroxychloride with 150 g of polyaluminumferric/ferrous chloride [Al Fe₀.25^(II) Fe₀.25^(III) (OH)₂.12 (Cl)₂.13 ]. After 20 minutes of mixing, an organic-inorganic adduct was obtained having:

pH=1.90,

Specific Gravity=1.195 g/cc,

Solids=25%,

Appearance=light brown liquid.

EXAMPLE NO. 51

The conditions of Example No. 49 were repeated in the presence of 30 g of polyethyleneamine with very high molecular weight (Mw) and 150g. of 40% FeCl₃ instead of HAlC. After 30 minutes of reaction, an organic-inorganic alloy polymer was obtained with:

pH=0.3,

Specific Gravity=1.210 g/cc,

Solids=30%

Appearance=clean dark brown color.

EXAMPLE NO. 52

The conditions of Example No. 46 were repeated by substituting the 37% HCl with 302 g (2.003 moles) of 65% phosphoric acid. The reaction was continued for 9 hours at 90°-95° C., then was cooled to room temperature resulting in polyguanylureaphosphate with:

pH=2.30,

Specific Gravity=1.218 g/cc,

Solids=47%

Appearance=water color.

EXAMPLE NO. 53

The conditions of Example No. 47 were repeated by substituting (PHAMS) with 330 g of hydroxyaluminumchloride (20% aq. solution). The end product has:

pH=2.25

Specific Gravity=1.185 g/cc,

Solids=38%

EXAMPLE NO. 54

To 300 g (50%) of polydiallyldimethylammoniumchloride (PDADMAC) was added during 10 minutes 300 g (50%) of polyhydroxyaluminumagnesiumsulfate (PHAMS) (41% aqueous solution). The composition was mixed for 20 minutes until the viscosity and pH remained constant. A light yellow color viscous adduct polymer was produced, having:

pH=2.32

Specific Gravity=1.185 g/cc

Solids=45%

EXAMPLE NO. 55

The conditions of Example No. 54 were repeated by substituting the (PHAMS) with polyhydroxyaluminumcalciumchloride (Al₇ Ca₀.04 (OH)₁₇.01 (Cl)₄) with: pH=2.45, and Specific Gravity=1.402 g/cc. The composition was mixed for 30 minutes when a product was produced having a water color to very light yellow color, with the characteristics:

pH=2.95

Specific Gravity=1.184 g/cc

Solids=56%

EXAMPLE NO. 56

The conditions of Example No. 54 were repeated by substituting the polyhydroxyaluminumagnesiusulfate (PHAMS) with 40% polyhydroxyaluminumchlorosilicate (PHAClSi). A light semiviscous adduct polymer was produced having:

pH=2.40

Specific Gravity=1.153 g/cc

Solids=48%

EXAMPLE NO. 57

The conditions of Example No. 54 were repeated by substituting the (PHAMS) with 48% polyhydroxyaluminumagnesiumchlorosulfate (PHAMCS); Al₄ Mg(OH)₆ (Cl)₄ (SO₄)₂. The end product has:

pH=2.05

Specific Gravity=1.170 g/cc

Solids=45%

Appearance=yellow color.

EXAMPLE NO. 58

To 400 g (54.56%) of the product made in Example 57 was added 100 grams of HCl (0.1 N) and mixed for 10 minutes. During a 15 minute period, 50 grams (6.82%) of the polyguanidine polymer produced in Example 25 was added. After a 10 minute reaction time, 183 grams of HCl (0.1 N) (38.62%) was added and mixed for 20 minutes. The end product has:

pH=1.8

Specific Gravity=1.100 g/cc

Solids=20%

Appearance=tint blue colloidal color.

EXAMPLE NO. 59

To 300 grams of polydiallyldimethylammoniumchloride (POLYDADMAC) (45.87%) was added during 12 minutes 100 grams of polyaluminumferrousferricchloride (15.28%). The composition was mixed for 15 minutes until the viscosity and pH remained constant. To this dark brown composition having a pH of 2.85 was slowly added 200 grams of HCl (0.1 N) (30.57%) followed by 54 grams of polyguanidine polymer made in Example 25 (8.28%). After 20 minutes, a semiviscous adduct polymer was produced having:

pH=2.0

Specific Gravity=1.036 g/cc

Solids=26% (by moisture)

Appearance=clear, light brown color (transparent)

EXAMPLE NO. 60

To the reactor described in Example 1 was charged 290 grams (2.0 moles) adipic acid, 200 grams (1.938 moles) diethylenetriamine, and 96.3 grams (5.35 moles) water. Aminopolyamide is made in accordance with Example No. 4 of U.S. Pat. No. 3,311,594, and 140 grams of such aminopolyamide having 50% solids is mixed with 29.4 grams of HCl (18% by weight). The composition is mixed for 15 minutes at 25° to 30° C., followed by the addition of 23.8 grams of polyhydroxyaluminumzincoxide chloride Al₃ (OH)₃ ZnO(OH)(Cl)₅. The reaction is continued for an additional 30 minutes, which produces an inorganic-organic alloy, having:

pH=3.2

Specific Gravity=1.095 g/cc

Appearance=light brown color, fluid

EXAMPLE NO. 61

The polyamide described in Example No. 58 is made by using:

    ______________________________________                                         1.    Diethylenetriamine                                                                             212.1 g 2.055 moles                                      2.    Water           77.8 g  4.322 moles                                      3.    Adipic acid     284. g  1.945 moles                                      4.  Under agitation and nitrogen blanket, the adipic acid is                       dissolved at 70-90° C.                                              5.  The composition is slowly heated to 120° C. and held for                1 hour.                                                                    6.  Then it is heated slowly to 165-175° C. and held for                    3 hours.                                                                   7.  The product is cooled to 150-155° C. when 426.1 g                       (23.672 moles) of H.sub.2 O is added and temperature held at                   95° C.-105° C. for 60 minutes.                               8.  A brown transparent aminopolyamide is obtained,                                having 50% solids.                                                         9.  The polymer is cooled to 30° C.                                     10. To 396 g. of amidopolyamine is added 100 g of polyfunctional                   polyamine (B,II/e C.sub.12 H.sub.26 N.sub.2 O.sub.2 Cl.sub.2) and              sufficient water                                                               to bring the solids to 30% bw.                                             11. The composition is heated to 90 to 95° C. for 2.5 hours and             then cooled.                                                               12. A strong cationic charged aminopolyamide is obtained                           by the structure believed to be:                                            ##STR19##                                                                      ##STR20##                                                                         where m ≧ 1, R = divalent aliphatic hydrocarbon, this                   intermediate product having: pH = 8.10, specific gravity =                     1.050 g/cc, Appearance = light brown color, Solids = 25%.                  13. To 100 g of the above polyaminoamide product, 1.30 g of HCl                    (18% bw) is added at the temperature 25 to 30° C.                   14. The agitation is continued for 20 minutes.                                 15. 20 g. of 20% hydroxyaluminumchloride (Al.sub.2 (OH).sub.5 (Cl) is              added.                                                                     16. The reaction is continued for an additional 30 minutes when                    the inorganic-organic alloy polymer is produced having:                        pH = 3.7, specific gravity = 1.1230 g/cc, Appearance =                         light yellow color.                                                        ______________________________________                                    

EXAMPLE NO. 63

300 g of the product made in Example No. 15 is diluted with 100 g of dionized water. Under agitiation was added 42.4 g of HCl (18% bw). To this solution was added during 10 minutes 25 g of the amineopolyamide made as in Example No. 61. The composition is mixed 30 minutes at room temperature. The product has: pH=3.0, Specific Gravity=1.130 g/cc, Appearance=light yellow color.

To 84% by weight of this composition is added slowly 16% by weight of hydroxyaluminumchloride (Al₂ (OH)₅ Cl) as 20% solution. The composition is mixed for 15 minutes, resulting in a product having:

pH=3.25,

Specific Gravity=1.105 g/cc,

Appearance=clear water color.

EXAMPLE NO. 64

To 959.1 g of 25% by weight solution of hydroxyaluminum sulfate (Al₂ (OH)₄ SO₄), having pH=2.55, is added 68.9 g of the aminepolyamide as made in Example No. 61. The reaction is carried out at 25° to 30° C. for 30 minuters, then the anion Cl⁻ is exchanged by multi aluminum anion composition such as [Al(OH)₂ (SO₄)]. The product has:

pH=2.80,

Specific Gravity=1.160 g/cc,

Appearance=light yellow color

EXAMPLE NO. 65

To 270 g 25% by weight of hydroxyaluminum chloride (Al₂ (OH)₅ Cl) with pH=4.0 is added during 10 minutes 20 g of the aminopolyamide made as in Example No. 61. After 30 minuters of mixing at 25° to 30° C. the adduct has:

pH=4.65,

Specific Gravity=1.104 g/cc,

Appearance=light yellow color.

To further exemplify and demonstrate the improved characteristics of the flocculating material disclosed above, numerous tests were conducted. These tests and their results are discussed below.

TEST I

Super concentrated acrylic sizing latex waste water from an ultrafiltration unit was treated with 600 parts per million (ppm) doses of conventional ferric chloride (FeCl₃) alum (aluminum sulfate-Al₂ (SO₄)₃, Al₂ (SO₄)₃ 18H₂ O) and the products I, II, and III. The results of this treatment are indicated below.

    __________________________________________________________________________                 After treatment                                                                with                                                                               with                                                           Before      38% 48.50%                                                                              with Product                                              Parameter                                                                            treatment                                                                            FeCl.sub.3                                                                         Alum I  II  III                                                                               IV  V                                           __________________________________________________________________________     Chemical                                                                       Oxygen                                                                               45963 34000                                                                              32000                                                                               6500                                                                              8100                                                                               5200                                                                              4500                                                                               12,000                                      DEMAND                                                                         (Cod)                                                                          __________________________________________________________________________

where:

I is polyhydroxyaluminumagnesiumchlorosulfate (PHAMCS) or (Al₄ Mg(OH)₆ (Cl)₄ (SO₄)₂).

II is 50% astringen, or hydroxyaluminumchloride (Al₂ (OH)₅ Cl); (trade name of Robinson Wagner Company, Inc.).

III is inorganic-organic alloy (PDADMAC/PHAMCS-see Example No. 54);

IV is inorganic-organic alloy polymer based on PDADMAC; polyhydroxyaluminumcalciumchloride (Al₇ Ca₀.04 (OH)₁₇.01 (Cl)₄). See Example No. 55.

V is PDADMAC (Polydiallyldimethyl ammoniumchloride).

The products III and IV provided highly satisfactory results with supernatant water clarity, no back pressure, very fast filtration, and low moisture on the sludge cakes, which make them very economical to be applied to a plant incineration system.

TEST II

Waste water from paper mill plant effluent (black liquor and bleach water (50/50) with color over 20,000 APHA was treated pH=6.5 with 200 milligram per liter doses. The results of this treatment are indicated below:

    ______________________________________                                                          Before  Color                                                 Product          Treatment                                                                              Removal (%)                                           ______________________________________                                                          20000                                                                          APHA                                                          Product V                87%                                                   Product VI               85%                                                   Product VII              86%                                                   Magnofloc (a):                                                                 C - 509 (Melamine resin) 64%                                                   585 - C (Polyamine)      53%                                                   Agefloc (b):                                                                   WT - 40 (PDADMAC)        55%                                                   Betz (c):                57%                                                   1275 (Polyamine)                                                               NALCO:                                                                         8102 (Polyamine)         70%                                                   ______________________________________                                    

Where

(V) is the product of Example No. 15,

(VI) is the product of Example No. 16,

(VII) is (2:1) ratio of the products made on Example 1 (Steps number 1 to 10 and Example No. 52.

Note that the products V and VI removed up to 90 to 93% of the color when 300 milligram per liter dosage was used.

(a) Magnofloc-Trade name of American Cyanamid Co.

(b) Agefloc-Trade name of C.P.S. Chemicals Company.

TEST III

Plant effluent waste water from paper mill plant with turbidity over 10,000 NTU was treated with 200 milligram per liter, pH=7.5. The results were as follows:

    __________________________________________________________________________                         Turbidity before                                                                        Turbidity after Treatment                         Product             treatment (NTU)                                                                         (NTU) No pH Adjustment                            __________________________________________________________________________                         10,000 N.T.U.                                              Product VII                                                                    (Example #36)                7.8                                               Product - VIII. (2:1) Example #1                                                                            7.8                                               (step #1 to 10) and Example #52                                                Product - IX. (Example #36)  6.5                                               Product - X (Example #24)    6.5                                               Product - V                  4.5                                               Product - XI. (Example #46)  4.5                                               Product - XII. (Example #49) 5.5                                               Product - XIII. (Example #50)                                                                               8.8                                               FeCl.sub.3 (30%)             42                                                Product - XIV (Polyferrousferricchloride)                                                                   15                                                Alum (48.5%)                 38                                                __________________________________________________________________________

TEST IV

Water used to wash the air in paint or lacquer spray booth in order to remove over-sprayed paint or lacquers was treated with 250 milligrams per liter (ppm) at pH=9 to 10, by a sodium aluminate adjustment, with the following detackifier compositions. The results are indicated below:

    ______________________________________                                                                  Detacki-                                                                              Observed                                                 Water   Paint  fication                                                                              Water Clarity                                  Product   mls     mls    Grade  Gardner Scale Color                            ______________________________________                                         Product XV                                                                               250     5.5    1      0                                              Product XVI                                                                              250     5.5    2      0                                              Product XVII                                                                             250     5.5    1      0                                              Product XVIII                                                                            100     2.18   1      0                                              Product XIX                                                                              100     2.18   3      3                                              ______________________________________                                    

where

XV is Maxichem--962 (a polyamine of Maxichem Inc.),

XVI is Maxichem--964 (a polyamine of Maxichem Inc.),

XVII is Maxichem--957,

XVIII is the product of Example No. 57 reacted with Maxichem-211 (a polyethyleneimine inorganic-organic alloy having total alkalinity 250 mg/g KOH),

XIX is Example I of U.S. Pat. No. 3,990,986 (Nalco Chemical Company)

The Gardner Color Scale is:

0--water color; 1--white; 2--slightly yellow; 3--yellow; 4--brownish yellow; 5--brown; 6--dark brown; 7--dark, blackish color.

Detackification grade units are arbitrarily defined as:

1--very good; 2--good; 3--fair; 4--poor; 5--unacceptable.

TEST V

A 5% aqua emulsion mixture (freon extracts 15,200 ppm) from Nylon Finishing product which is composed from white mineral oil, peanut oil, oleic acid, glycerol oleate, butyl stearate, diethylene glycol, alkanolamine, solvent, sulfuric acid, caustic soda and formaldehyde was prepared. 1200 ppm of the following products were mixed for 90 minutes. After 2 hours, the two resulting layers were separated. The freon extracts from the water layer were evaluated:

    __________________________________________________________________________             Before                                                                              Treated with the Products: at pH = 6.3                            Freon   treatment            Astrigen                                                                            Alum                                                                               AlCl.sub.3                               extraction                                                                             ppm  Example #9                                                                            #16                                                                               #61                                                                               #65                                                                               50%  48.5                                                                               10% Al.sub.2 O.sub.3                     __________________________________________________________________________     5% emulsion                                                                            15,200                                                                              155    105                                                                               100                                                                               93 379  failure                                                                            failure                                  mixture of                                                                     Organic soap (ppm)                                                             Fiber Finishing                                                                __________________________________________________________________________                             B/ Treated with the Products:                                                  Example #1                                                                            Magnafloc                                                                            PDADMAC                                                           Step 1-10                                                                             575   WT-40                                     __________________________________________________________________________                             3351   2688  1715                                                              (ppm)                                                  __________________________________________________________________________

From the foregoing, it is readily apparent that I have invented a group of novel inorganic-organic alloy copolymers, which are well suited for waste water treatment and other environmental uses. 

What is claimed is:
 1. Water-soluble inorganic-organic alloy polymer adduct composition for purification of potable water, acid rain water, paper mill effluent, industrial waste water, industrial waste liquids, solids and semiliquids, water-borne waste and paint, said composition having the formula:

    A·B·C·D

wherein A=Me_(m) ^(II) Me_(n) ^(III) (OH)_(p) (SO₄)_(y) (Aci).sub.(2m+3n)-p-2y ; B= ##STR21## C=(PAM)_(z) (PAM-PAD)_(t+z) ; D=(PQAM)_(w) ; Me_(m) ^(II) is selected from the divalent cation group comprising Mg, Zn, Ca, and Fe²⁺ ; m=0 to 5; Me_(n) ^(III) is a tri- or more valent metal selected from the group comprising Fe, Al, and Al-Zr complexes; n=1 to 20; Aci is selected from the monovalent anionic group comprising Cl⁻, Br⁻, I⁻, and NO₃ ; PAM=polyamine; PAD=polyamide; PQAM=polyquaternized polymer; p=0 to 75; x=2 to 98; y=0 to 15 z=0 to 95% percent by weight of polyamine; t=0 to 95% percent by weight of polyamide; w=0 to 98% percent by weight of polyquaternized polymer; R₁ =bridge cationic or multiple organic cationic charge or mixture thereof.
 2. A composition according to claim 1 wherein A is from 5% to 95% by weight of the total alloy composition, and is selected from the group comprising: polhydroxyaluminumchloride, hydroxyaluminumchloride, polyhydroxyaluminumagnesiumchloride, polyhydroxyaluminumagnesiumsulfate, hydroxyaluminumagnesium sulfate, hydroxyaluminumsulfate, polyhydroxyaluminumzincoxidechloride, polyhydroxyaluminumchlorosulfate, polyhydroxymagnesiumchlorosulfate, polyaluminumferricchloride, polyaluminumferrouschloride, polyaluminumchloridesulfate, polyhydroxyaluminumchloridesilicate, and polyhydroxyaluminumsodiumsulfophosphate.
 3. A composition according to claim 1 wherein B is selected from the group comprising polymers or resins made from guanidine, dicyandiamide, or cyanoguanidine compounds.
 4. A composition according to claim 1, wherein D (PQAM) is selected from the group comprising aqueous solutions of the quaternary ammonium compounds and their ethylenically unsaturated and their (co)polymerizable compounds.
 5. Water-soluble inorganic-organic alloy polymer adduct composition for purification of potable water, acid rain water, paper mill effluent, industrial waste water, industrial waste liquids, solids and semiliquids, water-borne waste and paint, said composition having the formula:

    A·B·C·D

wherein A=0 to 98% by weight of polyhydroxyaluminumsulfate inorganic adducts polymer; B=2 to 98% by weight of polymers of copolymerized dicyandiamide; C=0 to 95% by weight of polyalkylamines, and 0 to 95% by weight of a mixture of polyalkylamine and an aqueous solution of cationic resin; and D=0to 95% by weight of an aqueous solution of a quaternary ammonium compound.
 6. Water-soluble inorganic-organic alloy polymer adduct composition for purification of potable water, acid rain water, paper mill effluent, industrial waste water, industrial waste liquids, solids and semiliquids, water-borne waste and paint, said composition having the formula:

    A·B·C·D

wherein A=0 to 98% by weight of aluminum chloride; B=2 to 98% by weight of polymers of copolymerized dicyandiamide; C=0 to 95% by weight of polyalkylamines, and 0 to 95% by weight of a mixture of polyalkylamine and an aqueous solution of cationic resin; and D=0 to 95% by weight of an aqueous solution of a quaternary ammonium compound.
 7. Water-soluble inorganic-organic alloy polymer adduct composition for purification of potable water, acid rain water, paper mill effluent, industrial waste water, industrial waste liquids, solids and semiliquids, water-borne waste and paint, said composition having the formula:

    A·B·C·D

wherein A=0 to 98% by weight of polyhydroxyaluminumchlorosilicate inorganic adduct polymer; B=2 to 98% by weight of polymers of copolymerized dicyandiamide; C=0 to 95% by weight of polyalkylamines, and 0 to 95% by weight of a mixture of polyalkylamine and an aqueous solution of cationic resin; and D=0 to 95% by weight of an aqueous solution of a quaternary ammonium compound.
 8. Water-soluble inorganic-organic alloy polymer adduct composition for purification of potable water, acid rain water, paper mill effluent, industrial waste water, industrial waste liquids, solids and semiliquids, water-borne waste and paint, said composition having the formula:

    A·B·C·D

wherein A=0 to 98% by weight of aluminumsulfate; B=2 to 98% by weight of polymers of copolymerized dicyandiamide; C=0 to 95% by weight of polyalkylamines, and 0 to 95% by weight of a mixture of polyalkylamine and an aqueous solution of cationic resin; and D=0 to 95% by weight of an aqueous solution of a quaternary ammonium compound. 